Microstructure and fracture toughness of Si3N4Â +Â graphene platelet composites
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Silicon nitride + 1 wt% graphene platelet composites were prepared using various graphene platelets (GPLs) as filler. The influence of the addition of GPLs on the microstructure development and on the fracture toughness of Si3N4 + GPLs composites was investigated. The GPLs with thickness from 5 nm to 50 nm are relatively homogeneously distributed in the matrix of all composites, however overlapping/bundle formation of GPLs was found, containing 2-4 platelets as well. The single GPLs and overlapped GPLs are located at the boundaries of Si3N4, and hinder the grain growth and change the shape of the grains. The fracture toughness was significantly higher for all composites in comparison to the monolithic Si3N4 with the highest value of 9.9 MPa m0.5 for the composite containing the GPLs with smallest dimension. The main toughening mechanisms originated from the presence of graphene platelets, and responsible for the increase in the fracture toughness values are crack deflection, crack branching and crack bridging.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of the European Ceramic Society - Volume 32, Issue 12, September 2012, Pages 3389-3397
Journal: Journal of the European Ceramic Society - Volume 32, Issue 12, September 2012, Pages 3389-3397
نویسندگان
Ján Dusza, Jerzy Morgiel, Annamária Duszová, Lenka Kvetková, Martin Nosko, Péter Kun, Csaba Balázsi,