Surface morphologic and structural analysis of IR irradiated silver

The microstructural morphological changes in laser irradiated targets are investigated. Nd:YAG laser (1064 nm, ∼12 ns nominal, 1.1 MW) is used to irradiate 4 N pure (99.99%) fine polished and annealed silver samples in ambient air and under vacuum ∼10−6 Torr. The laser spot size and power density at tight focus are 12 μm and 3×1011 W/cm2, respectively. SEM micrographs and X-ray diffractograms of the exposed and unexposed targets reveal the surface texture and structural changes, respectively. Amongst the ablation mechanisms involved, exfoliation and hydrodynamic sputtering are found to be dominant. Surface modifications appear in the form of craters and ripples formation. Heat is conducted non-uniformly through narrow channels at the surface. Thermal stresses induced by the laser do not disturb inter planar distance of the target. On the other hand irradiation causes significant variations in grain size and diffracted X-rays intensities.