Vibrational and electronic properties of single-walled and double-walled boron nitride nanotubes

We calculated IR, nonresonance Raman spectra and vertical electronic transitions of the zigzag single-walled and double-walled boron nitride nanotubes ((0,n)-SWBNNTs and (0,n)@(0,2n)-DWBNNTs). In the low frequency range below 600 cm−1, the calculated Raman spectra of the nanotubes showed that RBMs (radial breathing modes) are strongly diameter-dependent, and in addition the RBMs of the DWBNNTs are blue-shifted reference to their corresponding one in the Raman spectra of the isolated (0,n)-SWBNNTs. In the high frequency range above ∼1200 cm−1, two proximate Raman features with symmetries of the A1g (∼1355 ± 10 cm−1) and E2g (∼1330 ± 25 cm−1) first increase in frequency then approach a constant value of ∼1365 and ∼1356 cm−1, respectively, with increasing tubes’ diameter, which is in excellent agreement with experimental observations. The calculated IR spectra exhibited IR features in the range of 1200–1550 cm−1 and in mid-frequency region are consistent with experiments. The calculated dipole allowed singlet–singlet and triplet–triplet electronic transitions suggesting a charge transfer process between the outer- and inner-shells of the DWBNNTs as well as, upon irradiation, the possibility of a system that can undergo internal conversion (IC) and intersystem crossing (ISC) processes, besides the photochemical and other photophysical processes.