• Effect of preparation conditions for light olefins production was studied.
• The catalyst containing 8% Fe/2.4%Mn/ZSM-5 showed the best catalytic performance.
• The reaction conditions were found 270 °C, 1 atm, H2/CO = 2/1 and GHSV = 2600 h−1.
In the present work, a series of iron based catalysts supported on ZSM-5 were prepared using incipient wetness method and tested for C2–C4 light olefins production from syngas (CO + H2). The effects of Fe and Mn loading, calcination conditions, different promoters, wt.% K as an optimal promoter and operational conditions on the catalytic performance of the optimal catalyst were investigated. It was found that the catalyst containing 8% Fe/2.4%Mn/ZSM-5 promoted with 2 wt.%K had the best catalytic performance for light olefins production. The best operational conditions were H2/CO = 2/1 M feed ratio, T = 270 °C, gas hourly space velocity (GHSV) = 2600 h−1 and 1 bar pressure. Catalysts and precursors were characterized by X-ray diffraction (XRD), transmission electron microcopy (TEM), thermal gravimetric analysis (TGA), temperature program reduction (TPR), Scanning electron microcopy (SEM), differential scanning calorimetry (DSC) and N2 adsorption–desorption measurements. The TPR spectrum for 8% Fe/2.4%Mn/ZSM-5 showed lower reduction temperatures respect to similar Fe–Mn catalysts.
In this study, a series of iron based nano catalysts supported on ZSM-5 were prepared using incipient wetness method and were tested for C2–C4 light olefins production. It was found out that catalyst containing 8% Fe/2.4%Mn/ZSM-5 promoted with 2wt. % K showed the best catalytic performance for C2–C4 light olefins production.Figure optionsDownload as PowerPoint slide
Journal: International Journal of Hydrogen Energy - Volume 40, Issue 43, 16 November 2015, Pages 14816–14825