![عکس صفحه اول مقاله: Hydrogen storage properties of nano-structured 0.65MgH2/0.35ScH2 Hydrogen storage properties of nano-structured 0.65MgH2/0.35ScH2](/preview/png/1274359.png)
The intermetallic compound Mg0.65Sc0.35 was found to form a nano-structured metal hydride composite system after a (de)hydrogenation cycle at temperatures up to 350 °C. Upon dehydrogenation phase separation occurred forming Mg-rich and Sc-rich hydride phases that were clearly observed by SEM and TEM with the Sc-rich hydride phase distributed within Mg/MgH2-rich phase as nano-clusters ranging in size from 40 to 100 nm. The intermetallic compound Mg0.65Sc0.35 showed good hydrogen uptake, ca. 6.4 wt.%, in the first charging cycle at 150 °C and in the following (de)hydrogenation cycles, a reversible hydrogen capacity (up to 4.3 wt.%) was achieved. Compared to the as-received MgH2, the composite had faster cycling kinetics with a significant reduction in activation energy Ea from 159 ± 1 kJ mol−1 to 82 ± 1 kJ mol−1 (as determined from a Kissinger plot). Two-dehydrogenation events were observed by DSC and pressure–composition-isotherm (PCI) measurements, with the main dehydrogenation event being attributed to the Mg-rich hydride phase. Furthermore, after the initial two cycles the hydrogen storage capacity remained unchanged over the next 55 (de)hydrogenation cycles.
► Nano-structured 0.65MgH2/0.35ScH2 hydrogen storage system.
► Derived from phase separation of Mg0.65Sc0.35 alloy.
► The phase separation resulting in uptakes of the order of a few minutes.
► Kinetics with significant reduction in activation energy of 82 ± 1 kJ mol−1.
► High reversible hydrogen capacity (up to 4.2 wt.%) and good cyclical stability.
Journal: International Journal of Hydrogen Energy - Volume 38, Issue 1, 11 January 2013, Pages 153–161