Fabrication and characterization of Cu–Ni–YSZ SOFC anodes for direct use of methane via Cu-electroplating

The Cu–Ni–YSZ cermet anodes for direct use of methane in solid oxide fuel cells have been fabricated by electroplating Cu into a porous Ni–YSZ cermet anode. The uniform distribution of Cu in the Ni–YSZ anode was obtained by electroplating in an aqueous solution mixture of CuSO4·5H2O and H2SO4 for 30 min with 0.1 A of applied current. When the Cu–Ni–YSZ anode was exposed to methane at 700 °C, the amount of carbon deposited on the anode decreased as the amount of Cu in the Cu–Ni solid solution increased. The power density (0.24 W/cm2) of a single cell with a Cu–Ni–YSZ anode was slightly lower in methane at 700 °C than the power density (0.28 W/cm2) of a single cell with a Ni–YSZ anode. However, the performance of the Ni–YSZ anode-supported single cell degraded steeply over 21 h because of carbon deposition, whereas the Cu–Ni–YSZ anode-supported single cell showed enhanced durability up to 200 h.