Facile fabrication of rutile monolayer films consisting of well crystalline nanorods by following an IL-assisted hydrothermal route

In this study, rutile films consisting of rectangular nanorods were facilely deposited on glass substrates from strongly acid solution of TiCl4. The highly ordered array of nanorods was realized in presence of ionic liquid (IL) of [Bmim]Br by following a hydrothermal process. In this process, Degussa P25 nanoparticles served as seeds that were pre-deposited on the substrates to facilitate the array of rutile nanorods. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and Raman spectrum were used to characterize the obtained nanorod films. The measurements showed that the nanorods were rectangular with width of 100–200 nm and length of more than 1 μm, and grew up typically along c-axis to form the arrays against the substrate. The presence of IL was found vital for the formation of rutile nanorods, and the suitable molar ratio of [Bmim]Br to TiCl4 ranged from 500:1 to 1500:1. The excessive [Bmim]Br may hinder the precipitation of rutile particles.

The rutile film consisting of rectangular nanorods is successfully deposited on glass substrate in presence of ionic liquid (IL) of [Bmim]Br. The nanorods were rectangular with width of 100–200 nm and length of more than 1 μm, which grew up typically along c-axis to form the arrays against the substrate.Figure optionsDownload as PowerPoint slide