NO2 gas sensing of flame-made Pt-loaded WO3 thick films

• Unloaded and Pt-loaded WO3 nanoparticles for NO2 gas detection were synthesized by flame spray pyrolysis (FSP).
• Gas sensing properties of the Pt-loaded WO3 sensors were excellent to those of the unloaded one.
• 0.25 wt% Pt-loaded WO3 sensor showed highest response to NO2 at low operating temperature of 150 °C.

Unloaded WO3 and 0.25–1.0 wt% Pt-loaded WO3 nanoparticles for NO2 gas detection were synthesized by flame spray pyrolysis (FSP) and characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM). The BET surface area (SSABET) of the nanoparticles was measured by nitrogen adsorption. The NO2 sensing properties of the sensors based on unloaded and Pt-loaded WO3 nanoparticles were investigated. The results showed that the gas sensing properties of the Pt-loaded WO3 sensors were excellent to those of the unloaded one. Especially, 0.25 wt% Pt-loaded WO3 sensor showed highest response to NO2 than the others at low operating temperature of 150 °C.

The response of 0.25 wt% Pt-loaded WO3 sensor was 637 towards NO2 concentration of 10 ppm at 150 °C.Figure optionsDownload as PowerPoint slide