Crystal structure of hexagonal SrAl2O4 at 1073 K

The crystal structure of SrAl2O4 at 1073 K was determined from conventional X-ray powder diffraction data using direct methods, and it was further refined by the Rietveld method. The structure was hexagonal (space group P63, Z=6Z=6) with a=0.89260(3) nm, c=0.84985(2) nm and V=0.58639(3) nm3. Final reliability indices were Rwp=7.87%, Rp=5.87% and RB=4.19%. The [AlO4] tetrahedra are linked to form trigonally distorted rings and they are joined in layers. These layers are stacked with a two-layer repeat and connected by the tetrahedral apices. All of the Sr atoms occupy the centers of the rings when viewed along the c-axis. The structure is described as a stuffed derivative of tridymite.