![عکس صفحه اول مقاله: Thermoelectric and microstructural properties of Pb0.9−xSn0.1GexTe compounds prepared by spinodal decomposition Thermoelectric and microstructural properties of Pb0.9−xSn0.1GexTe compounds prepared by spinodal decomposition](/preview/png/1330832.png)
Three samples of Pb0.9−xSn0.1GexTe with x=0.25, 0.35, 0.6 were prepared by heating the mixtures above the melting point of the constituent elements followed by quenching in water. The x=0.6 sample is close to the center of the immiscibility region, while the x=0.25 and 0.35 samples are in the Pb rich region inside the spinodal miscibility gap. Microstructural investigations using Powder X-ray Diffraction, Scanning Electron Microscopy and Energy Dispersive X-ray Spectroscopy revealed both GeTe-rich and PbTe-rich phases. The samples were uniaxially hot pressed and the thermoelectric properties were characterized in the temperature range 2–400 K using a commercial apparatus and from 300 to 650 K with a custom designed setup. The best sample (x=0.6) reached zT≈0.6 at 650 K, while the x=0.25 and 0.35 samples showed thermal instability at elevated temperatures.
Spinodal decomposition in the GeTe–SnTe–PbTe system demonstrated by SEM and EXS images.Figure optionsDownload as PowerPoint slideHighlights
► Investigation of Pb-rich part of the spinodal miscibility gap in PbTe–SnTe–GeTe.
► zT=0.6 at 650 K reproduced for Pb0.3Sn0.1Ge0.6Te.
► Pb-rich phases shown to be thermally instable.
► Thermoelectric property characterization at low and high temperature.
► Microstructural investigations using PXRD, SEM, EDX and PSM.
Journal: Journal of Solid State Chemistry - Volume 184, Issue 5, May 2011, Pages 1172–1175