Two real ternary lithium gold indides LiAu2In and Li280Au22In130 (Li0.65Au0.05In0.30) were found in the Li–Au–In system. They are isostructural to the respective Ag-alloys. LiAu2In crystallizes in the MnCu2Al-type structure (Fm-3m, Heusler phase, a=6.4982(8) Å, based on single crystal XRD-data) and Li280Au22In130 in the Li278Ag40In114-type structure (F-43m, a=19.9970(2) Å, based on powder XRD-data). The analogy of the two ternary systems Li–Au–In and Li–Ag–In is additionally reaffirmed by the wide homogeneity range of the pseudoternary solid solution with NaTl-type structure (Zintl phase),which expands not only in the direction of the quasibinary cut Li(AuxIn1−x) with 0≤x≤0.5, but also into the directions of both higher and lower Li-concentrations.
Two real ternary compounds (1: Heusler phase, 2: n=6 variant of a cubic n×n×n W-type superstructure) together with one pseudoternary compound (3: Zintl phase with its broad homogeneity range).Figure optionsDownload as PowerPoint slideHighlights
► “Real” ternary phases were found in the Li–Au–In systems: LiAu2In and Li280Au22In130.
► The homogeneity range of “pseudoternary” Li(AuxIn1−x) extends to the binary phase x=0.
► The three-element sets, both Li, Au, In and Li, Ag, In, are compound formers⁎. (*in the definition of Villars et al., J. Alloys Compd. 317–318, 2001, 26).
Journal: Journal of Solid State Chemistry - Volume 184, Issue 5, May 2011, Pages 1328–1332