• A noncentrosymmetric borate Ag3B5O9 is accessible via high-pressure synthesis.
• Ag3B5O9 is the second high-pressure silver borate.
• Ag+⋯Ag+ distances in Ag3B5O9 clearly indicate the presence of argentophillic interactions.
Single crystals of Ag3B5O9 were obtained via high-pressure synthesis at 3 GPa and 600 °C, using a Walker-type multianvil high-pressure device. Ag3B5O9 crystalizes with a=674.7(2), b=943.5(2), c=1103.5(2) pm, V=0.7025(2) nm3, and Z=4 in the noncentrosymmetric space group P212121 (no. 19). The orthorhombic structure was refined from 3740 independent reflections with R1=0.0496 and wR2=0.587 (all data). It is built up from infinite corner-sharing chains of BO4 tetrahedra along the a axis, which are interconnected by BO3 groups to form a network. In the structure, three crystallographically independent sites are occupied with Ag+ cations exhibiting argentophillic interactions. The synthetic conditions as well as the results of the single crystal structure analysis are presented.
Noncentrosymmetric silver borate: During investigations in the system Ag–B–O, a new noncentrosymmetric silver borate Ag3B5O9 was discovered. The new structure type is built up from corner-sharing BO3 and BO4 groups, forming a network. Argentophillic interactions are clearly indicated by the Ag+⋯Ag+ distances present in the structure.Figure optionsDownload as PowerPoint slide
Journal: Journal of Solid State Chemistry - Volume 225, May 2015, Pages 114–119