![عکس صفحه اول مقاله: A TEM investigation of the (Bi1−xSrx)Fe3+O3−x/2, 0.2≤x≤0.67, solid solution and a suggested superspace structural description thereof A TEM investigation of the (Bi1−xSrx)Fe3+O3−x/2, 0.2≤x≤0.67, solid solution and a suggested superspace structural description thereof](/preview/png/1331684.png)
A careful transmission electron microscopy (TEM) investigation of an incommensurately modulated member of the (Bi1−xSrx)Fe3+O3−x/2□x/2, 0.2≤x≤0.67, solid solution has been carried out. High resolution (HR) TEM imaging is used to show the presence of at least 6-fold twinning on a rather fine (∼5 nm) scale. The (3+1)-d superspace group symmetry is suggested to be Pmmm(0,12,γ) or one of the non-centrosymmetric sub-groups thereof, namely P2mm(0,12,γ), Pm2m(0,12,γ), Pmm2(0,12,γ) and P222(0,12,γ). A superspace construction is then used to propose the nature of the local compositional ordering and, hence, of the oxygen-deficient slab that intergrows with the perovskite slab to produce the observed solid solution phase. The proposed compositional superspace atomic surfaces can be used to produce model structures at any composition within the solid solution range.
Typical 〈100〉p zone axis EDP typical of the (Bi1−xSrx)Fe3+1O3−x/2□x/2, x∼0.55, sample.Figure optionsDownload as PowerPoint slide
Journal: Journal of Solid State Chemistry - Volume 182, Issue 8, August 2009, Pages 2176–2184