• The high-pressure behaviors of AlN:Mg and AlN:Co nanowires have been investigated.
• The pressure-induced wurtzite-to-rocksalt phase transitions have been observed.
• The phase transition pressures are lower than that of pure AlN nanowires.
• The distinct high-pressure behaviors are ascribed to the dopants.
• The vacancy defects and substitution defects influence structural stability.
High-pressure behaviors of AlN:Mg and AlN:Co nanowires have been investigated by in situ angle dispersive synchrotron X-ray diffraction up to 41.5 GPa and 38.2 GPa, respectively. Their corresponding pressure-induced wurtzite-to-rocksalt phase transitions start at 17.7 GPa and 15.0 GPa and complete at 33.2 GPa and 31.0 GPa, respectively. The phase-transition routes are not affected by the doped ions, while the phase transition pressures are lower than that of pure AlN nanowires. The distinct high-pressure behaviors are ascribed to the doped ions, which reduce the formation energy of cation vacancies and induce Al vacancies defects together with substitution defects, resulting in lattice distortion and affecting structural stability and phase transition pressure.
The high-pressure behaviors of AlN:Mg and AlN:Co nanowires have been investigated by in situ angle dispersive synchrotron X-ray diffraction.Figure optionsDownload as PowerPoint slide
Journal: Journal of Solid State Chemistry - Volume 202, June 2013, Pages 33–37