Nano/micro-sized coordination polymer La(1,3,5-BTC)(H2O)6 with controllable morphologies have been successfully prepared on a large scale via a simple solution phase method at room temperature. By rationally adjusting the synthetic parameters such as concentration, molar ratio of reactants, surfactant, and solvent, the La(1,3,5-BTC)(H2O)6 with 3D flowerlike, wheatearlike, spherical, sheaflike, taillike, bundlelike hierarchical architectures, and 1D nanorods can be selectively prepared. More interestingly, the photoluminescence color of codoped Eu3+ and Tb3+ lanthanum 1,3,5-benzenetricarboxylate phosphors can be easily tuned from red, orange, yellow, green-yellow to green by changing co-doping concentration of activator ions, making the material has potential applications in building minioptoelectronic devices, biomedicine, and color display fields.
La(1,3,5-BTC)(H2O)6 with 3D flowerlike, wheatearlike, spherical, sheaflike, taillike, bundlelike architectures, and 1D nanorods were selectively prepared; color-tunable photoluminescence from red to green was also realized by co-doping Eu3+ and Tb3+.Figure optionsDownload as PowerPoint slide
Journal: Journal of Solid State Chemistry - Volume 183, Issue 10, October 2010, Pages 2309–2316