Superstructure of hollandite KxMg(8+x)/3Sb(16−x)/3O16 (x≈1.76)

Single crystals of KxMg(8+x)/3Sb(16−x)/3O16 (x≈1.76) with a hollandite superstructure were grown. Ordering schemes for guest ions (K) and the host structure were confirmed by the structure refinement using X-ray diffraction intensities. The space group is I4/m and cell parameters are a=10.3256(6), c=9.2526(17)Å with Z=3. Superlattice formation is primarily attributed to the Mg/Sb occupational modulation in the host structure. Mg/Sb ratios at two nonequivalent metal sites are 0.8977/0.1023 and 0.1612/0.8388. Two types of the cavity are seen in the tunnel, where parts of K ions deviate from the cavity center along the tunnel direction. Probability densities for K ions in the two cavities are different from each other, which seems to have arisen from the Mg/Sb modulation.

Mg/Sb occupational modulation in a superstructure of hollandite KxMg(8+x)/3Sb(16−x)/3O16 (x≈1.76) was clarified by the X-ray diffraction technique. The Mg/Sb ratio is 0.8977/0.1023 at the M1 site and 0.1612/0.8388 at the M2.Figure optionsDownload as PowerPoint slide