Divergent effects of static disorder and hole doping in geometrically frustrated β-CaCr2O4

The gallium substituted and calcium deficient variants of geometrically frustrated β-CaCr2O4, β-CaCr2–2xGa2xO4 (0.02≤x≤0.25) and β-Ca1−yCr2O4 (0.075≤y≤0.15), have been investigated by X-ray powder diffraction, magnetization and specific heat measurements. This allows for a direct comparison of the effects, in a geometrically frustrated magnet, of the static disorder that arises from non-magnetic substitution and the dynamic disorder that arises from hole doping. In both cases, disturbing the Cr3+ lattice results in a reduction in the degree of magnetic frustration. On substitution of Ga, which introduces disorder without creating holes, a gradual release of spins from ordered antiferromagnetic states is observed. In contrast, in the calcium-deficient compounds the introduction of holes induces static ferrimagnetic ordering and much stronger perturbations of the β-CaCr2O4 host.

Scaled plot of the temperature dependence of the inverse susceptibility for β-CaCr2−2xGa2xO4 (closed symbols) and β-Ca1−yCr2O4 (open symbols). Data sets depicted in the same color contain equivalent amounts of Cr3+.Figure optionsDownload as PowerPoint slide