Remote activation by green-light irradiation of shape memory epoxies containing gold nanoparticles

• Gold nanoparticles (Au NPs) stabilized with PEO chains were synthesized.
• Au NPs were dispersed in a shape memory epoxy (SME) previously studied.
• Remote activation of the SME was produced by green-light irradiation.
• Shape recovery was produced after a few seconds employing 0.01 wt% NPs (5 nm).
• Epoxy chemistry was adapted to disperse Au NPs stabilized with dodecyl chains.

Shape memory epoxies (SMEs) that can be remotely activated by the use of green light, are described. An epoxy matrix based on on diglycidylether of bisphenol A (DGEBA cured with a mixture of n-dodecylamine (DA) and m-xylylenediamine (MXDA), exhibits excellent shape memory properties as described in a previous paper (Leonardi et al., 2011). Au NPs with an average diameter close to 5 nm could be uniformly dispersed in this matrix using poly(ethylene oxide) (PEO) chains as stabilizer. These NPs showed a significant photothermal effect even at very low concentrations (0.01 wt% as metallic gold), when irradiated with a 532 nm laser at a power close to 2 W/cm2. Under these conditions, a bended bar (1.4-mm thickness) recovered its initial shape in a few seconds. This formulation may be used to build up devices with the necessary mechanical strength and with the possibility to produce shape recovery by remote activation using green light. A second example was analyzed employing an amphiphilic epoxy matrix to produce a uniform dispersion of Au NPs stabilized with dodecyl chains (average diameter close to 3 nm). A bar (1.4-mm thickness) of the SME with 0.04 wt% Au NPs (as metallic gold) showed a fast recovery of its initial shape by irradiation with a 532 nm laser at a power close to 2 W/cm2. This example shows the feasibility of adapting the epoxy chemistry to disperse Au NPs stabilized with different ligands and obtained through robust synthetic methods.

Figure optionsDownload as PowerPoint slide