Studies on optimizing sesquioxide contents to enhance luminescence efficiency of Pr3+ ions in PbO−PbF2−B2O3 glass system

• Pr3+ doped lead oxy fluoro borate glasses mixed with Y2O3, Sc2O3 and Al2O3 were prepared.
• Information on structural changes was obtained using IR spectra.
• Optical absorption, PL spectra and decay curves were recorded.
• Luminescence peak intensity is increased with increase in the concentration of M2O3.
• Highest luminescence efficiency was observed for Y2O3 mixed glasses.

Pr3+ doped lead oxy fluoro borate glasses mixed with three sesquioxides (M2O3) viz. Y2O3, Sc2O3, Al2O3 of different concentrations (0–10 mol%) have been synthesized. The preliminary understanding over the structural modifications due to the insertion of the sesquioxides in the glass network could be obtained by IR spectral investigations. The optical absorption, luminescence spectra and fluorescence decay curves of these glasses were studied as functions of concentration of M2O3. The luminescence spectra of these glasses have exhibited the bands due to 3P0 → 3F2, 3F3, 3H6, 3H4, 3H5 transitions of Pr3+ ions. From these spectra, the radiative parameters viz., spontaneous emission probability A, the total emission probability AT, the radiative lifetime τ, the fluorescent branching ratio β of different transitions originated from 3P0 level of Pr3+ ions have been evaluated. A considerable enhancement in the luminescence emission corresponding to 3P0 → 3H6, 3F2 transitions has been observed with increase in the concentraion of M2O3 up to 8.0 mol%. The increase has been attributed to the possible declusterization of Pr3+ ions by M3+ ions in the glass network. The comparison of emissive characteristics of the glasses mixed with three sesquioxides indicated the highest luminescence efficiency for Y2O3 mixed glasses among the three series glasses studied and this has been explained in terms of different degrees of variations in the structural modifications in the vicinity of Pr3+ ion in the glass network.

Photoluminescence spectra of PbO–PbF2–B2O3 glasses doped with 1.0 mol% of Pr2O3 mixed with different concentrations of M2O3 recorded at room temperature.Figure optionsDownload as PowerPoint slide