High temperature induced phase transitions in Sr2ZnWO6 and Sr2CoWO6 double perovskite oxides: Raman spectroscopy as a tool
موضوعات مرتبط
مهندسی و علوم پایه شیمی شیمی آلی
پیش نمایش صفحه اول مقاله
High temperature induced phase transitions in Sr2ZnWO6 and Sr2CoWO6 double perovskite oxides: Raman spectroscopy as a tool
چکیده انگلیسی

In this paper we report high-temperature (up to 550 °C) Raman spectroscopy of phase transitions in Sr2MWO6 (M = Zn, Co) double perovskite oxides. For Sr2ZnWO6 modes centered at 137 cm−1, 152 cm−1, merge around 80 °C. The same behavior was observed for the 436 cm−1 and 447 cm−1 modes. The mode centered at 854 cm−1 shows a change in the slope at the same temperature, thus indicating a first order phase transition from the monoclinic (P21/n) to tetragonal (I4/m) structure. With increasing temperature, a little change in the slope of the temperature dependence of mode centered at 855 cm−1 is observed around 480 °C which might be a sign of the second phase transition in Sr2ZnWO6 (tetragonal (I4/m) to cubic (Fm-3m)). The temperature dependence of the full width at half maximum (FWHM) of the most intense modes in Sr2ZnWO6 spectra was studied. The width behaves linearly as a function of temperature with a break observed in the slope of the width of the modes at 80 °C; thus, showing the first phase transition occurrence. For Sr2CoWO6 the transition from tetragonal (I4/m) structure to cubic (Fm-3m) phase is accompanied by considerable changes in the temperature dependence of modes centered at 438 cm−1 and 845 cm−1. The transition was observed around 420 °C.


► Synthesis and characterization of Sr2MWO6 (M = Zn, Co) double perovskites.
► High temperature studies of double perovskite using Raman spectroscopy.
► Temperature induced phase transitions in these materials.