Simple synthesis of mesoporous carbon with magnetic nanoparticles embedded in carbon rods

Magnetically separable ordered mesoporous carbon containing magnetic nanoparticles embedded in the carbon walls was synthesized using a simple synthetic procedure. The resulting magnetically separable mesoporous carbon was denoted as M-OMC (magnetically separable ordered mesoporous carbon) poly(pyrrole) with residual Fe2+ ions in the mesoporous channel was converted to carbon material containing superparamagnetic nanoparticles. The size of the magnetic nanoparticles obtained was restricted by the channel size of the SBA-15 silica template, which resulted in the generation of superparamagnetic nanoparticles embedded in the carbon rods. The blocking temperature of M-OMC is 110 K. Pore size and textural property of M-OMC is similar to that of hexagonally ordered mesoporous carbon fabricated using SBA-15 silica as a template. The saturation magnetization of M-OMC is ca. 30.0 emu/g at 300 K, high enough for magnetic separation.