![عکس صفحه اول مقاله: Dispersion of tungsten oxide on SCR performance of V2O5WO3/TiO2: Acidity, surface species and catalytic activity Dispersion of tungsten oxide on SCR performance of V2O5WO3/TiO2: Acidity, surface species and catalytic activity](/preview/png/148702.png)
• Presence of bulk WO3 on titania surface leads to deficiency of Brønsted acid sites.
• Two-dimension VOx has a tendency to anchor onto titania surface in vicinity of WOx.
• WOx shows compressing effects on monolayer VOx species at high vanadium loadings.
• NH3-SCR performance is mainly dependent on vanadium contents of VW/TiO2 catalysts.
Effects of tungsten on vanadium-based catalysts were studied under differently dispersed conditions of tungsten oxide on titania surface. Acidity, surface species and NH3-SCR performance over commercial WO3/TiO2 and V2O5WO3/TiO2 have been investigated. The incomplete dispersion of tungsten oxide gives rise to the formation of crystalline WO3 on titania surface, and the mounts of surface Brønsted acid sites decrease consequently. From the TPR and Raman spectra, it is indicated that two-dimensional vanadium species exhibits a tendency to moderately anchor onto titania surface in the immediate vicinity of tungsten species. It is also found that amorphous tungsten oxide has different impacts on the dispersion of vanadium species over titania surface at variable loadings of vanadia. At low vanadium loadings, amorphously distorted tungsten species show promoting effects on the formation and dispersion of two-dimensional vanadium species. With vanadium loadings increasing, amorphous tungsten species exert compressing effects on surface vanadium species and lead to the aggregation of vanadium oxide.
Figure optionsDownload as PowerPoint slide
Journal: Chemical Engineering Journal - Volume 225, 1 June 2013, Pages 520–527