Cathodoluminescent and nonlinear optical properties of undoped and erbium doped nanostructured ZnO films deposited by spray pyrolysis

We have deposited zinc oxide (ZnO) and erbium doped zinc oxide (ZnO:Er) thin films on heated glass substrates using spray pyrolysis technique. The effect of erbium dopant on structural, morphological, luminescent and nonlinear optical properties was studied. The deposited films have been analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), ex situ compositional analysis (ESCA), profilometry, cathodoluminescence (CL) and third harmonic generation (THG) measurements. All films were polycrystalline, having a preferential growth orientation along the ZnO (0 0 2) plane, with a corresponding average crystallite size of less than 41 nm. Addition of erbium can effectively control the film surface morphology and its cathodoluminescent properties. The films containing low erbium concentration show a uniform surface covered with hexagonal shaped grains and a strong UV light emission intensity as well as TH response. In contrast, when the erbium doping ratio exceeds 3%, a porous surface with columnar textural growth becomes more pronounced, and a substantial reduction of the cathodoluminescent and TH response. A strong TH signal was obtained for the film with good crystalline quality at the concentration of 2%. Third order nonlinear optical susceptibility (χ〈3〉) values of the studied materials were in the remarkable range of 10−12 esu.