Fatigue behaviors and damage mechanism of a Cr-Mn-N austenitic steel
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Four-point bending fatigue tests were conducted on a CrMnN austenitic steel at room temperature, at frequency of 20Â Hz and the stress ratio of RÂ =Â 0.1, in air. The fatigue strength of this CrMnN austenitic steel was measured to be 503Â MPa in the maximum stress from the SN curve obtained. It was found that multi-site crack nucleation took place on the surface of the steel during fatigue, and that the crack population (i.e., fatigue weak-links) was found to be a Weibull function of the applied stress. Usually only one or two of the initiated cracks could lead to the final failure of the samples. Most of the cracks were initiated at the {111}<110> primary slip bands, especially within coarse grains. The cracks were deflected at grain boundaries, which effectively resisted short crack growth and arrested most of the short cracks in the alloy. It can be anticipated that grain refinement could further enhance the fatigue properties of the alloy.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 691, 15 January 2017, Pages 103-109
Journal: Journal of Alloys and Compounds - Volume 691, 15 January 2017, Pages 103-109
نویسندگان
Z. Lv, P. Cai, T. Yu, Y. Jin, H. Zhang, W. Fu, T. Zhai,