Enhanced mechanical properties and rolling formability of fine-grained Mg-Gd-Zn-Zr alloy produced by equal-channel angular pressing
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Enhanced mechanical properties and rolling formability of fine-grained Mg-Gd-Zn-Zr alloy produced by equal-channel angular pressing Enhanced mechanical properties and rolling formability of fine-grained Mg-Gd-Zn-Zr alloy produced by equal-channel angular pressing](/preview/png/1608813.png)
چکیده انگلیسی
A fine-grained Mg-1.8Gd-1Zn-0.1Zr (at.%) alloy with long-period stacking ordered (LPSO) phase was obtained via solid-solution(SS) treatment plus multi-pass equal-channel angular pressing(ECAP). The effects of post-ECAP rolling on microstructure change and deformation characteristic of the Mg alloy were investigated. The results showed that the fine-grained alloy after 16 ECAP passes at 658Â K had a yield strength of 334.4Â MPa with an elongation of 22.5%. Grain refinement with LPSO formation simultaneously improved the strength and ductility of the ECAPed alloy, indicating a good plastic formability. The ECAPed Mg sheet was easily rolled at 773Â K from 1.5Â mm to 0.24Â mm in thickness without edge cracking. After rolling, the fine-grained Mg alloy exhibited higher tensile strength with appropriate elongation. The post-ECAP rolling has been successfully used in the high productivity of Mg thin sheet with good mechanical properties.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 643, 15 September 2015, Pages 28-33
Journal: Journal of Alloys and Compounds - Volume 643, 15 September 2015, Pages 28-33
نویسندگان
Fumin Lu, Aibin Ma, Jinghua Jiang, Jing Chen, Dan Song, Yuchun Yuan, Jianqing Chen, Donghui Yang,