Phase equilibria in CaO–B2O3–TiO2 system at 1373 K and 1473 K were investigated using quenching method followed by X-ray diffraction and scanning electron microscopy (SEM) equipped with energy dispersive analysis (EDS). Isothermal sections in CaO–B2O3–TiO2 system at 1373 K and 1473 K were experimentally constructed. No ternary oxide compounds were found in this system. The liquidus composition of CaO–B2O3–TiO2 system at 1373 K and 1473 K were determined. The section at 1373 K contains one liquid region, three solid–liquid coexistence regions and five subsolid regions. The section at 1473 K contains one liquid region, five solid–liquid coexistence regions and three subsolidus regions.
► Phase equilibria in CaO–B2O3–TiO2 system at 1373 K and 1473 K were investigated using quenching method followed by XRD and SEM–EDS.
► Isothermal sections in CaO–B2O3–TiO2 system at 1373 K and 1473 K were experimentally constructed.
► The liquidus compositions of CaO–B2O3–TiO2 system at 1373 K and 1473 K were determined.
Journal: Journal of Alloys and Compounds - Volume 562, 15 June 2013, Pages 171–175