Sr1−x(Bi, Na)x/2Bi2Nb2O9 (SBNBNO, x = 0, 0.2, 0.4 and 0.6) ceramics were prepared by the conventional solid-state route. X-ray diffraction analyses (XRD) and Raman spectroscopy indicated that all specimens have a single phase with perovskite-type orthorhombic structure. The piezoelectric activity and Curie temperature of SrBi2Nb2O9 (SBN) ferroelectric ceramics are significantly improved by bismuth and sodium modification. The piezoelectric coefficient d33 of the Sr0.6(Bi, Na)0.2Nb2O9 (SBNBN4) specimen was found to be 22 pC/N, which is higher than the d33 values (about 12 pC/N) of SBN specimen. Moreover, the SBNBN4 specimen exhibited the excellent temperature stability of piezoelectric properties. In order to confirm the nature of the piezoelectric properties enhanced, the relationship between the structure and electrical properties was discussed.
► The piezoelectric properties of SBN are enhanced by (Bi, Na) modification.
► The d33 and Tc of SBNBN4 are 22 pC/N and 586.5 °C, respectively.
► The d33 of SBNBN4 have better temperature stability.
► The better piezoelectric activities are induced by larger lattice distortion.
Journal: Journal of Alloys and Compounds - Volume 550, 15 February 2013, Pages 335–338