Microstructure evolution and thermal stability of an Fe-based amorphous alloy powder and thermally sprayed coatings

High velocity oxy-fuel (HVOF) thermal spraying has been used to produce coatings of an Fe–18.9%Cr–16.1%B–4.0%C–2.8%Si–2.4%Mo–1.9%Mn–1.7%W (in at.%) alloy from a commercially available powder (Nanosteel SHS7170). X-ray diffraction (XRD), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM) were employed to investigate the powder, as-sprayed coatings and annealed coatings which had been heated to temperatures in the range of 550–925 °C for times ranging from 60 to 3900 min. Microhardness changes of the coatings were also measured as a function of annealing time and temperature. The powder was found to comprise amorphous and crystalline particles; the former had a maximum diameter of around 22 μm. The coating was composed of splat like regions, arising from rapid solidification of fully molten powder, and near-spherical regions from partially melted powder which had a largely retained its microstructure. The amorphous fraction of the coating was around 50% compared with 18% for the powder. The enthalpies and activation energies for crystallization of the amorphous phase were determined. Crystallization occurred in a two stage process leading to the formation of α-Fe (bcc), Fe1.1Cr0.9B0.9 and M23C6 phases. DSC measurements showed that the first stage occurred at 650 °C. Annealing the coating gave a hardening response which depended on temperature and time. The as-sprayed coating had a hardness of 9.2 GPa and peak hardnesses of 12.5 and 11.8 GPa were obtained at 650 and 750 °C, respectively. With longer annealing times hardness decreased rapidly from the peak.