The phase diagram Mo–Ta–As was studied in two partial isothermal sections at 1050 °C (in the As-rich corner) and at 1400 °C (As-poor alloys) using powder X-ray diffraction and electron probe microanalysis. A complete solid solution was found to exist between isostructural Mo5As4 and Ta5As4 and the ternary solubility of Mo in Ta3As at 1400 °C was determined. A ternary phase MoxTa1−xAs with MnP-type structure was found to exist in the As-rich part of the system. Lattice parameters were investigated as a function of composition for (Mo,Ta)5As4 and for MoxTa1−xAs. Additional experiments of chemical vapor transport (CVT) from 1000 °C to 900 °C using different ternary source compositions and I2 and Br2 (PtBr2) as transport agents were performed. Only Ta compounds were found in the sink and no ternary transport was observed.
Journal: Journal of Alloys and Compounds - Volume 480, Issue 2, 8 July 2009, Pages 397–402