We report, high surface area (up to 200 m2/g) nanocrystalline niobium oxide (so called p-Nb2O5) synthesized by ‘chimie douce’ route and its importance in enhancing the hydrogen sorption properties of MgH2. p-Nb2O5 induces faster kinetics than commonly used commercial Nb2O5 (c-Nb2O5) when ball milled with MgH2 (named (MgH2)catalyst) by reducing the time of desorption from 35 min in (MgH2 )c-Nb2O5(MgH2 )c-Nb2O5 to 12 min in (MgH2 )p-Nb2O5(MgH2 )p-Nb2O5 at 300 °C. The BET surface area of as-prepared Nb2O5 was tuned by heat treatment and its effect on sorption properties was studied. Among them, both p-Nb2O5 and Nb2O5:350 (p-Nb2O5 heated to 350 °C with a BET specific surface area of 46 m2/g) desorb 5 wt.% within 12 min, exhibiting the best catalytic activity. Furthermore, thanks to the addition of high surface area Nb2O5, the desorption temperature was successfully lowered down to 200 °C, with a significant amount of desorbed hydrogen (4.5 wt.%). In contrast, the composite (MgH2 )c-Nb2O5(MgH2 )c-Nb2O5 shows no desorption at this “low” temperature.
Journal: Journal of Alloys and Compounds - Volume 460, Issues 1–2, 28 July 2008, Pages 507–512