Structural, magnetic and magnetotransport properties of La0.8Sr0.2MnO3/xLaMnO3 composites

The effect of LMO doping on the structure, magnetic and magnetotransport properties of La0.8Sr0.2MnO3 (LSMO)/xLaMnO3 (LMO) has been investigated. Two types of LSMO/xLMO composites, named as SLx (low temperature sintered samples) and SHx (high temperature sintered samples) samples, were prepared by different sintering temperature and solid-state reaction method. The presence of LMO at the grain boundaries increases the disordered states at the surface of the grains and therefore the magnetization and transition temperature decrease by increasing the amount of LMO doping level. Results show that the rate of decreasing of transition temperature is much more for high temperaure sintered samples. Also the resistivity of samples increases by the increase of LMO doping level. Results also show that the LMO doping has an effect on a low field magnetoresistance (LFMR). The value of LFMR increases for low doping level of 0 ≤ x ≤ 15, for SLx samples and 0 ≤ x ≤ 10 for SHx samples. Also LFMR decreases at high doping level. The spin dependent tunneling and scattering at the interfaces of the grain boundaries are responsible for the increase of LFMR at low doping level, while reduction of LFMR at high doping level may result from the grain boundary becoming too thick for electron tunneling.