![عکس صفحه اول مقاله: Bi doping effects on the physical properties of Pr0.6Sr0.4Mn1−xBixO3 (0 ≤ x ≤ 0.2) manganese oxides Bi doping effects on the physical properties of Pr0.6Sr0.4Mn1−xBixO3 (0 ≤ x ≤ 0.2) manganese oxides](/preview/png/1624682.png)
Structural, magnetic and magneto-caloric properties of Pr0.6Sr0.4Mn1−xBixO3 (0.0 ≤ x ≤ 0.2) powder samples have been investigated. X-ray powder diffraction showed that all our synthesized samples are single phase and crystallize in the orthorhombic symmetry with Pbnm space group. The unit cell volume increases with increasing Bi content. Bi doping leads to a weakening of the ferromagnetic (FM) ordering at low temperature, the Curie temperature Tc decreases from 310 K for x = 0.0 to 225 K for x = 0.2. The critical exponent γ deduced from the M(H) curves is found to be γ = 0.33 for Pr0.6Sr0.4Mn0.9Bi0.1O3 sample. A large magneto-caloric effect has been detected with a maximum of magneto-entropy change, |ΔSmax|, of 0.95 and 2 J/kg K at 1 and 8 T, respectively, at 255 K for a Bi doping amount of 0.1.
Journal: Journal of Alloys and Compounds - Volume 452, Issue 2, 20 March 2008, Pages 195–199