The conductivities of several donor-doped SrTiO3 based oxides, which were prepared in air, were studied in a reducing atmosphere at high temperature. The conductivities of all specimens increased slowly with time at 1000 °C in 9% H2/N2, even after 100 h. Nb-doped SrTiO3 showed relatively fast reduction and high conductivity compared with the other SrTiO3 based oxides. The conductivity of Nb-doped SrTiO3 was ca. 50 S cm−1 at 500 °C after reduction at 1200 °C. After strong reduction, the conductivity of Nb-doped SrTiO3 was almost independent of the oxygen partial pressure at 500–800 °C, while that of La-doped SrTiO3 dropped immediately on exposure to air. The conduction behavior of Nb-doped SrTiO3 was explained by reduction of Ti4+ and/or Nb5+ and the relatively slow oxygen diffusibility.
Journal: Journal of Alloys and Compounds - Volume 439, Issues 1–2, 31 July 2007, Pages 232–236