Evidence of oxygen vacancy and possible intermediate gap state in layered α-MoO3 single-crystal nanobelts

Multilayered meso-structured MoO3 nanobelts have been synthesized by thermally oxidizing a molybdenum chip in a reduced oxygen atmosphere, with a view to disclosing the existence of oxygen vacancy and understanding the mechanism behind the influence of oxygen vacancy on the electronic structure of molybdenum oxides. Based on the measurements from X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscope (SEM) and transmission electron microscope (TEM), it is found that the as-grown sample is single-crystal α-MoO3 with a (001) preferred orientation, which shows an irregular belt-like morphology being composed of some ~20 nm single-crystal thin layers. The present sample includes a lot of oxygen vacancies in the lattice, as evidenced by the considerably reduced coordination number of the central Mo atoms from X-ray absorption spectra (XAS) as well as the red shift of the main Raman peaks. The existence of the oxygen vacancies are further tested by the photoluminescence (PL) results as the main emission peak shows an obvious red shift with the corresponding optical band gap reduced to 2.3 eV. Very importantly, an extra emission positioned at 738 nm (1.68 eV) is believed to originate from the recombination of the electrons from the intermediate band (IB) to the valence band (VB), and the formation of the IB in the gap is also caused by oxygen-ion vacancies.