Effect of Al incorporation on the structural, morphological, optoelectronic and transport properties of PbS thin films

Doping of PbS thin films with different metal atoms produce considerable changes in structural and material properties that make them useful in the technology of thin film devices. The goal of this work is to study the effects of doping on the structural, morphological, optoelectronic and transport properties of PbS thin films as a function of Al3+ concentration. Thin films of pure and Al doped PbS nanoparticles are prepared on soda lime glass substrates by chemical bath deposition technique. The Al content in aqueous solution is varied from 0 to 20 mg. XRD analysis of the films revealed significant enhancement in crystallinity and crystallite size up to an optimum concentration of doping. Films are polycrystalline with crystallite size 19–32 nm, having face centered cubic structure. The optical band gap energy exhibits a decreasing trend and is shifted from 2.41 to 1.34 eV with increasing Al content. The room temperature conductivity of the as-deposited PbS films is in the range of 0.78×10−8 to 0.67×10−6(Ω cm)−1 with a maximum for optimum Al content. The Al doped PbS thin film, which we synthesize with optimum Al concentration of 15 mg is found to be a most suitable material for solar control coating applications.