Samples of Co1−xZnxLayFe2−yO4, 0.1≤x≤0.9, y =0.25, were prepared using standard ceramic technique. X-ray investigations were carried out in order to assure the formation of the samples in single spinel phase. The dielectric constant ε´ was measured at different temperatures as the function of frequencies ranging from 100 kHz to 3 MHz for the investigated samples. The dielectric constant ε´ increases with temperature up to transition temperature T(ε´) and decreases with frequency. ε´ decreases also with increasing Zn content. Tε´ increases continuously with Zn content depending on frequency. The magnetic susceptibility for the prepared samples was measured using Faraday's method at different temperatures as the function of the magnetic field intensity. The magnetic parameters were calculated from the magnetic susceptibility data, in the temperature range 300–800 K at three different magnetic field intensities of 720, 1070 and 1380 Oe. The data show a decrease in the magnetic susceptibility till it reaches the Curie temperature TC. It is noted that the effective magnetic moment (μeff.) gives the same trend as that of TC with Zn content.
Journal: Physica B: Condensed Matter - Volume 405, Issue 2, 15 January 2010, Pages 727–731