![عکس صفحه اول مقاله: Radiation synthesis and characterisation of the network structure of natural/synthetic double-network superabsorbent polymers Radiation synthesis and characterisation of the network structure of natural/synthetic double-network superabsorbent polymers](/preview/png/1886473.png)
In this study radiation synthesis and characterisation of the network structure of acrylic acid sodium salt/locust bean gum, (AAcNa/LBG) natural/synthetic double-network super absorbent polymers were investigated. Quartet systems composed of acrylic acid sodium salt/locust bean gum/N,N methylene bis acrylamide/water (AAcNa/LBG/MBAAm/water) were prepared at varying degree of neutralisations (DN) by controlling the DN value of AAc and irradiated with gamma rays at ambient temperature at a very low dose rate. The influences of the DN on the swelling and network properties were examined. It was observed that the DN strongly affected the gelation and super absorption properties of the gels. Molecular weight between crosslinks (M¯c), effective crosslink density (νe) and mesh size (ξ) of SAPs were calculated from swelling and shear modules data obtained from compression and oscillatory frequency sweep tests. M¯c values obtained from the uniaxial deformation experiments were very close to those obtained from the oscillatory shear experiments excluding the completely neutralised gel system. It was concluded that the uniaxial compression technique could be used for the characterisation of the network structure of a hydrogel as along with the rheological analyses; however, a very precise control of the gel size was also needed.
► Radiation synthesis and characterisation of AAcNa/LBG super absorbent polymers described.
► Influences of the DN on the swelling and network properties were examined.
► Molecular weight between crosslinks and effective crosslink density of SAPs were calculated.
► Suitability of rheology technique for the characterisation of hydrogels were demonstrated.
Journal: Radiation Physics and Chemistry - Volume 81, Issue 9, September 2012, Pages 1378–1382