Synthesis of proton conductive membranes based on inorganic–organic hybrid structure bound with phosphonic acid

Proton conductive inorganic–organic hybrid membranes were synthesized from styrene derivatives of alkoxysilane and ethyl 2-[3-(dihydroxyphosphonyl)-2-oxopropyl] acrylate (EPA) through copolymerization followed by sol–gel reaction. Self-standing, homogeneous and transparent hybrid membranes with chemically bound phosphonic acid groups were synthesized. FT-IR analysis exhibited the hybrid membranes included phosphonic acid groups. 13C and 29Si NMR studies indicated that alkoxysilyl functionalized styrene derivatives were not only copolymerized with EPA but also condensed yielding Si–O–Si linkages by sol–gel reaction. TG–DTA analysis revealed that these membranes were thermally stable up to 200 °C in dry O2. The proton conductivities of the hybrid membranes increased with phosphonic acid content and temperature. The P/Si ratio of the membrane was dependent on the number of alkoxy group in the starting alkoxysilane. The hybrid membrane from (dimethylmethoxysilylmethyl)styrene (DMMSMS(M))/EPA = 1/6 revealed proton conductivities of 6.3 × 10−3 and 2.4 × 10−4 S cm−1 at 68.0% relative humidity and 18.8% relative humidity, respectively, at 140 °C.