Investigation of a transparent chromate (III) passive film on electroless Ni–P coating by XPS and electrochemical methods
موضوعات مرتبط
مهندسی و علوم پایه مهندسی شیمی مهندسی شیمی (عمومی)
پیش نمایش صفحه اول مقاله
Investigation of a transparent chromate (III) passive film on electroless Ni–P coating by XPS and electrochemical methods
چکیده انگلیسی

A transparent passive film on electroless nickel phosphorus coating (ENPC) was obtained in a chromate (Cr3+) bath. An ENPC sample passivated in a Cr6+-containing bath was used for comparison. The corrosion properties were tested by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). SEM, XPS, and EDX were employed to analyze the chemical composition and surface morphology of the films. SEM results indicate that the passive film is too thin to be observed by SEM. The potentiodynamic polarization tests show that the corrosion currents of the two passivated samples are only about 1/25 of the un-passivated coating. The XPS analysis illustrate that the Cr6+-treated film comprises Cr, Ni and O, while the Cr3+-treated film is made up of Cr, C, O, Ni, P and N. High-resolution XPS analysis show that, both in Cr6+-treated and Cr3+-treated films, element Cr is only in the form of trivalent compounds, no hexavalent chromium existing. By XPSpeak analyzing, trivalent chromium compounds on the two treated surfaces were fitted as Cr(OH)3 and Cr2O3. However, for the Cr3+ and Cr6+ passivation routes, the Cr(OH)3 and Cr2O3 contents in passive films are widely divergent.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Electrochimica Acta - Volume 54, Issue 26, 1 November 2009, Pages 6718–6724
نویسندگان
, , , ,