Platinum-modified titanium anodes for the electrolytic destruction of nitric acid

Three sets of electrodes, namely Pt electroplated Ti (PET) and diffusion annealed PET (DAPET) of plating thickness 3, 5, 7 and 10 μm and thermochemically glazed mixed oxide coated titanium anode (MOCTA-G) were evaluated for their performance, with a view to optimizing the current density conditions for maximum efficiency during the electrolytic destruction of nitric acid. In the acid killing by electro-reduction process, concentration of nitric acid in the high level waste (HLW) from the spent nuclear fuel reprocessing plant was brought down from about 4 to 0.5 M in order to reduce the amount of HLW by subsequent evaporation and to minimise the corrosion in waste tanks during storage of the concentrated waste solution. The electrochemical reduction of 4 and 8 M nitric acid to near neutral conditions was carried out with the above-said anodes and Ti cathode at various cathodic current densities ranging from 10 to 80 mA cm−2. At current densities below 15 mA cm−2 MOCTA-G electrode worked satisfactorily, whereas PET and DAPET electrodes could withstand and function well at much higher cathodic current densities (up to 80 mA cm−2). The life assessment of a 3 μm thick PET electrode at a cathodic current density of 60 mA cm−2 in 8 M HNO3 for a period of 110 h showed no failure. Phase identification of the plated electrodes was done by XRD measurements and their surface morphology was investigated by SEM.