Zinc hexacyanoferrate film as an effective protecting layer in two-step and one-step electropolymerization of pyrrole on zinc substrate

The two-step and one-step electrosynthesis processes of polypyrrole (PPy) films on the zinc substrate are described. The two-step process includes (i) the zinc surface pretreatment with hexacyanoferrate ion in the aqueous medium in order to form a zinc hexacyanoferrate (ZnHCF) film non-blocking passive layer on the surface and with the view to prevent its reactivity and (ii) electropolymerization of pyrrole on the ZnHCF|Zn-modified electrode in aqueous pyrrole solution. In this context, both the non-electrolytic and electrolytic procedures were adapted, and the effect of some experimental conditions such as supporting electrolyte, pH and temperature of the solution at the zinc surface pretreatment step as well as pyrrole concentration and electrochemical techniques at the polymerization step was investigated. By optimizing the experimental conditions in both steps, we have obtained a homogeneous and strongly adherent PPy films on the zinc substrate.The one-step process is based on the use of an aqueous medium containing Fe(CN)64− and pyrrole. The ferrocyanide ion passivates the substrate by formation of ZnHCF film during the electropolymerization process of pyrrole and therefore makes it possible to obtain strongly adherent PPy films, with controlled thickness, either by cyclic voltammetry or by electrolysis at constant current or constant potential without any previously treatment of the zinc electrode surface. The polypyrrole films deposited on the zinc electrode were characterized by cyclic voltammetry and scanning electron microscopic (SEM) measurement.