In the present work, the use of three Slovak poor metakaolin sands with different metakaolin content (36.0% (MK-1), 31.5 (MK-2) and 40.0% (MK-3)) and specific surface has been deeply studied as mineral addition for Portland cement. The percentage of metakaolin sands in the blended cements was 10%, 20% and 40%.The pozzolanic tests confirm that the three metakaolin sands show a high pozzolanic activity, comparable to a commercial metakaolin and silica fume. With respect to the rheological behaviour, metakaolin sand–blended-cement pastes fit to Herchel–Bulkley model and their yield stress increases as the metakaolin content increases. MK-3 sand with the highest pozzolanic activity and highest specific surface induces the highest increase of the yield stress.From the calorimetric results it is concluded that the addition of MK-1 and MK-2 sands to Portland cement induces a delay up to 2 h of the precipitation of the main hydration products in the blended-cement pastes and decreases the maximum heat evolution rate. On the contrary, the incorporation of 40% of MK-3 sand shortens 6 h its apparition and increases significantly the maximum heat evolution rate. Additionally, the presence of the metakaolin sands reduces the heat released during the hydration process with respect to non-blended-cement pastes.The incorporation of metakaolin sand induces a decrease of the mechanical strength, being the decrease higher as the metakaolin sand content increases although they also produce a refinement in the pore structure and a decrease of the permeability.
Journal: Construction and Building Materials - Volume 24, Issue 5, May 2010, Pages 791–802