Moisture-induced stresses perpendicular to grain in cross-sections of timber members exposed to different climates

In variable humidity conditions, wood absorbs or desorbs moisture from the air. Unless the change in humidity is very slow, this will develop moisture gradients in the wood sections. These gradients will develop stresses due to constrained swelling or shrinkage strains. These stresses are named moisture-induced stresses. The present paper investigates the main parameters affecting such moisture-induced stresses, including the type of climate, the size of the timber cross-section, and the type of protective coating. A first attempt to identify moisture-induced stresses in different European climatic regions was made. For each climatic region, relative humidity and temperature histories were identified, and characteristic and mean values of yearly and daily variations were calculated. Using a finite element model implemented in Abaqus, the moisture content and stress distribution were computed on different timber cross-sections exposed to the climatic regions and protected with different types of coating. A Fickian moisture transfer model was used to compute the moisture distribution, and a mechanical model for time-dependent behaviour of wood was implemented to calculate the corresponding stress distribution. The variation of moisture was found to result in stresses of magnitudes that would probably cause cracking of wood in the perimeter of any uncoated cross-section size. The use of a protective coating, however, reduced considerably the moisture-induced stresses, and can be regarded as an effective protective measure to avoid cracking due to humidity variations. Considering European climates, Northern climates were found to result in higher surface tensile stresses than Southern climates.

► Air humidity variations cause moisture gradients and moisture-induced stresses (MIS) in timber sections.
► Europe divided into climatic regions with Northern climates more severe than Southern climates in terms of MIS.
► Larger moisture content variations and MIS in smaller size and uncoated sections.
► MIS perpendicular to the grain likely to cause cracking of wood in the perimeter of any uncoated section size.
► Use of a protective coating is as an effective way to reduce MIS and avoid cracking of wood.