Ordered mesoporous Bi2WO6 (M-Bi2WO6) with nanocrystalline walls was fabricated for the first time by a silica-templated nanocasting method with bismuth nitrate and phosphotungstic acid as precursors. The as-prepared mesoporous Bi2WO6 sample exhibited a much higher photocatalytic activity than the conventional hydrothermally synthesized nanoscale Bi2WO6 (HR-Bi2WO6) on the degradation of phenol which is quite toxic but widely used and slowly degradable in the environment. Almost 97% of the phenol molecules were degraded within 60 min along with the sharp decrease of total organic carbon (TOC) in 100 mL of phenol solution (20 mg/L) under visible-light irradiation. Compared with HR-Bi2WO6 sample, the M-Bi2WO6 sample exhibited a negative shift of conduction band edge potential and faster charge transfer property which helped to improve the photocatalytic performance.
Figure optionsDownload as PowerPoint slideHighlights
• Ordered mesoporous Bi2WO6 is firstly realized by nanocasting method.
• It is used for photocatalytic oxidation of organic contaminants.
• Its photocatalytic activity is significantly better than nonporous powder.
• Electrochemical studies reveal the reasons for its high photocatalytic activity.