In this study novel flame retardant boron phosphate (BPO4)/polyimide composites were prepared. 4,4â²-Oxydianiline (ODA) was reacted with 3,3â²,4,4â²-benzophenonetetracarboxylic dianhydride (BTDA) in dimethyl formamide (DMF) and mixed with BPO4 particles to obtain a series of polyamic acids, meanwhile, corresponding polyimides were synthesized via the thermal imidization technique. The amount of BPO4 in the composite films was varied from 0Â wt% to 10Â wt%. The structure, thermal and surface properties of the polyimide films were characterized by means of ATR-FTIR, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and scanning electron microscopy (SEM). The flame retardancy of the composite materials was examined by limiting oxygen index (LOI) measurements and UL-94 VTM tests. Result showed that the LOI values of composites increased from 28 to 39. Furthermore, proton conductivity of polyimide films was measured by the four probe technique. The composite membrane containing 3Â wt% of BPO4 showed a conductivity of 0.4Â mS/cm at room temperature.
Journal: Polymer Degradation and Stability - Volume 98, Issue 5, May 2013, Pages 927-933