Indoor accelerated and outdoor weathering of polystyrene-b-(ethylene-co-butylene)-b-styrene (SEBS) was studied by infrared spectroscopy. Accelerated conditions involved simultaneous exposure of specimens to ultraviolet-visible radiation between 295 nm and 450 nm and each of four temperature/relative humidity (RH) environments, i.e., (a) 30 °C ± 1 °C at <1% RH, (b) 30 °C ± 1 °C at 80% RH, (c) 55 °C ± 1 °C at <1% RH, and (d) 55 °C ± 1 °C at 80% RH. Outdoor exposure was conducted in Gaithersburg, MD, in two different time periods. Similar photooxidative mechanisms were operative under all conditions. In the case of indoor accelerated exposure, the rate of photooxidation was found to depend strongly on temperature. Unlike the exposure at 55 °C, moisture-assisted photooxidation was insignificant at 30 °C. A quantitative study on the synergistic effect of environmental stressors revealed that the degrading effect of combined temperature and moisture on photooxidation was greater than the sum of the two effects exerted independently. Outdoor weathered specimens exhibited significantly slower photooxidation. Acceleration of photooxidation ranged from 2.5 to 10 times in comparison to the outdoor exposure, depending on the indoor accelerated conditions.
Journal: Polymer Degradation and Stability - Volume 96, Issue 6, June 2011, Pages 1104-1110