Inherent flame retardation of bio-based poly(lactic acid) by incorporating phosphorus linked pendent group into the backbone

The molecular design for inherently flame-retardant poly(lactic acid) (IFR-PLA) was outlined and achieved by chemically incorporating an effective organophophorus-type flame retardant (FR) into the PLA backbone via the chain extension of the dihydroxyl-terminated prepolymer with 1, 6-hexamethylene diisocyanate (HDI). The structure of IFR-PLA was characterized by 1H- and 31P-nuclear magnetic resonance (NMR) and Fourier transform infrared (FTIR) spectroscopy. IFR-PLA was further blended with the commercial PLA to prepare flame retardant PLA blends (PLA-FR blend). The relevant properties of IFR-PLA and PLA-FR blends were evaluated by differential scanning calorimetry (DSC), thermal gravimetric analysis (TGA), limiting oxygen index (LOI) measurements and UL-94 tests. The thermal analysis revealed that the char yield of IFR-PLA and PLA-FR blend above 400 °C was greatly enhanced compared to that of pure PLA. The LOI value was significantly improved from 19 for pure PLA to 29 when 1 wt% of phosphorus content was introduced and all IFR-PLA samples achieved V-0 rating in the UL-94 tests. PLA-FR blends had an LOI value of 25-26 and UL-94 V-2 rating at 20 wt% of IFR-PLA content. The tensile strength of all the FR PLA systems was ca. 60 MPa. The method used in this study provided a novel route to permanently flame retard PLA.