Thermal stability of aromatic polyesters prepared from diphenolic acid and its esters

The thermal performance of aromatic polyesters (poly(DPA-IPC), poly(MDP-IPC) and poly(EDP-IPC)) prepared from isophthaloyl chloride (IPC) with diphenolic acid (DPA) and its esters were studied with DSC and TG, and the decomposition mechanism of poly(DPA-IPC) were investigated using FTIR and integrated TG/FTIR analyses. As compared with ordinary aromatic polyesters, poly(DPA-IPC) has lower glass transition temperature (159 °C) and much lower thermal stability. It starts to decompose at about 210 °C and is characterized by two-stage thermal decomposition behavior, with active energies of decomposition of 206 kJ/mol and 389 kJ/mol, respectively. The analyses of the decomposition process and products indicate that the pendent carboxyl groups in poly(DPA-IPC) are responsible for its low thermal stability. Accordingly, a decomposition mechanism for the first stage is proposed. With this knowledge in mind, we capped the carboxyl groups in DPA with methyl and ethyl groups to prepare poly(MDP-IPC) and poly(EDP-IPC) from methyl diphenolate and ethyl dipenolate. As expected, these two polymers exhibit obviously improved thermal stability, with onset decomposition temperature of about 300 °C.