Material propertiesEffects of partial replacement of silicone rubber with flurorubber on properties of dynamically cured poly(vinylidene fluoride)/silicone rubber/flurorubber ternary blends

Blends of poly(vinylidene fluoride) (PVDF), silicone rubber (SR) and flurorubber (FKM) were prepared via peroxide dynamic vulcanization. The effect of FKM loading on the morphology, mechanical properties, crystallization behavior, rheology and dynamic mechanical properties of the PVDF/SR/FKM ternary blends was investigated. A “network” was observed in the PVDF/SR binary blends, which disappeared in the ternary blends, but a core-shell-like structure was formed. The mechanical properties were significantly improved. The Izod impact strength of PVDF/SR/FKM blend with 19 wt% FKM was 18.3 kJ/m2, which was 3-4 times higher than the PVDF/SR binary blend. The complex viscosity and storage modulus of the PVDF/SR/FKM blends decreased with increasing FKM content, hence the processability was improved. The increase of FKM content seemed to show a favorable effect on the crystallization of the PVDF component. It promoted the nucleation process of PVDF, leading to increased polymer crystallization rate and higher crystallization temperature. The glass-rubber transition temperature of the PVDF phase moved to a lower temperature.