Transreactions in poly trimethylene terephthalate/bisphenol-A polycarbonate (PC) blends analysed by pressure-volume-temperature measurements

The effect of annealing on the miscibility and thermal properties of poly trimethylene terephthalate (PTT)/bisphenol-A polycarbonate (PC) blends was examined using pressure-volume-temperature (PVT) measurements. The PTT/PC blends were thermally annealed at 260 °C for different times to induce various extents of transesterification reactions between the two polymers. The non-annealed blends are immiscible and exhibit the thermal properties of the blend components. Upon annealing, the original semi-crystalline morphology transforms to an increasingly amorphous nature. PVT and WAXS analysis confirmed that the PTT/PC blends completely lost their crystallinity when annealed at 260 °C for a period of 120 min or longer, indicating the formation of random co-polyesters due to chemical transreactions between the PTT and PC. The further increase in the specific volume with annealing time also indicates that after reaching a completely amorphous co-polymer the transesterification continuous until a fully random copolymer is formed.